廠家(產(chǎn)地):韓國(guó)可隆 牌號(hào):K300 用途級(jí)別:注塑級(jí)
性能項(xiàng)目 |
測(cè)試條件 |
測(cè)試方法 |
數(shù)值/描述 |
單位 |
|
機(jī)械性能 |
拉伸強(qiáng)度(引張強(qiáng)度) |
|
ASTM D638/ISO 527 |
640 |
kg/cm2(MPa)[Lb/in2] |
斷裂伸長(zhǎng)率 |
|
ASTM D638/ISO 527 |
|
% |
|
拉伸模量 |
|
ASTM D638/ISO 527 |
|
kg/cm2(MPa)[Lb/in2] |
|
拉伸屈服伸長(zhǎng)率(延伸率) |
|
ASTM D638/ISO 527 |
65 |
% |
|
拉伸斷裂伸長(zhǎng)率(延伸率) |
|
ASTM D638/ISO 527 |
|
% |
|
彎曲模量(彎曲彈性率) |
|
ASTM D790/ISO 178 |
|
kg/cm2(MPa)[Lb/in2] |
|
彎曲強(qiáng)度 |
|
ASTM D790/ISO 178 |
920 |
kg/cm2(MPa)[Lb/in2] |
|
洛氏硬度 |
|
ASTM D785 |
|
|
|
IZOD 缺口沖擊強(qiáng)度 |
1/4" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
|
1/4" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
1/8" 23℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
1/8" -30℃ |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
Charpy沖擊強(qiáng)度 |
23℃ (缺口) |
ASTM D256/ISO 179 |
7.0 |
kg·cm/cm(J/M)ft·lb/in |
|
-30℃(缺口) |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
23℃(無(wú)缺口) |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
-30℃(無(wú)缺口) |
ASTM D256/ISO 179 |
|
kg·cm/cm(J/M)ft·lb/in |
||
物性性能 |
比重(密度) |
|
ASTM D792/ISO 1183 |
1.41 |
|
成型收縮率 |
|
ASTM D955 |
|
% |
|
熔融指數(shù)(流動(dòng)系數(shù)) |
200℃/5kg |
ASTM D1238/ISO 1133 |
9.0 |
g/10min |
|
220℃/10kg |
ASTM D1238/ISO 1133 |
|
g/10min |
||
吸水率 23℃/24H |
|
ASTM D570/ISO 62 |
0.22 |
% |
|
熱性能 |
熱變形溫度 |
退火 |
ASTM D648/ISO 75 |
|
℃(℉) |
未退火 |
ASTM D648/ISO 75 |
|
℃(℉) |
||
維卡軟化點(diǎn) |
|
ASTM D1525/ISO R306 |
|
℃(℉) |
|
熔點(diǎn) |
|
- |
166 |
℃(℉) |
|
燃燒性(率) |
|
UL94 |
|
|
|
線性膨脹系數(shù) |
|
ASTM D696/ISO 11359 |
|
mm/mm.℃ |
|
電氣性能 |
介電常數(shù) |
100HZ |
ASTM D150/IEC 60250 |
|
|
1MHZ |
ASTM D150/IEC 60250 |
|
|
||
體積電阻率 |
|
ASTM D257/IEC 60093 |
|
Ω.cm |
|
表面電阻率 |
|
ASTM D257/IEC 60093 |
|
Ω |
|
耐電弧性 |
|
ASTM D495/IEC 60112 |
|
|