SABIC美國沙伯 PPE+PA6 NORYL GTX679
| 產(chǎn)品型號： |
GTX679 |
| 產(chǎn)品規(guī)格： |
PPE |
| 產(chǎn)品品牌： |
沙伯基礎(chǔ)創(chuàng)新（美國） |
沙伯基礎(chǔ)創(chuàng)新塑料(SABIC Innovative Plastics) PPE+PA6、GTX679、GTX674PC、GTX4610、GTX673、GTX678、GTX8730、GTX902D、GTX975、GTX989、NX0031、Noryl PPO, Lexan PC, Valox PBT, Ultem PEI, Cycoloy PC/ABS, Xylex PC/PET, Xenoy PC/PBT/PET.
|
Compare
|
Contact Us
|
|
|
NORYL GTX? Resin
|
|
|
|
Grades
|
Description
|
|
|
GTX4610
|
PPE+PA, Glass,
Datasheet
Product Data:
Auto Data:
|
|
|
GTX673
|
PPE+PA, Conductive,
Datasheet
Product Data:
Auto Data:
|
|
|
GTX678
|
PPE+PA, Flame Retardant, Conductive, Heat Stabilized, Impact Modified, Nonhalogenated,
Datasheet
Product Data:
Auto Data:
|
|
|
GTX8730
|
PPE+PA, Glass, Conductive,
Datasheet
Product Data:
Auto Data:
|
|
|
GTX902D
|
NORYL GTX902D is a GTX902E with smaller shaped pellets.
Datasheet
Product Data:
Auto Data:
|
|
|
GTX975
|
18% mineral filled conductive NORYL GTX.
Datasheet
Product Data:
Auto Data:
|
|
|
GTX989
|
PPE+PA, Conductive, High Impact,
Datasheet
Product Data:
Auto Data: Auto Specification
|
|
|
NX0031
|
PPE+PA, conductive with high impact
Datasheet
Product Data:
Auto Data:
|
|
|
|
NORYL GTX GTX679 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to allow for primer-less electrostatic painting. GTX679 has improved impact/elongation and the mineral content enables the material to be used in structural applications replacing metal or thermoset resins. The material is only available in black.
|
|
|
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 5 mm/min
|
650
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
630
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
3
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
4
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min
|
45300
|
kgf/cm2
|
ASTM D 638
|
|
Flexural Stress, brk, 1.3 mm/min, 50 mm span
|
1100
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
40700
|
kgf/cm2
|
ASTM D 790
|
|
Tensile Stress, yield, 5 mm/min
|
61
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 5 mm/min
|
61
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 5 mm/min
|
2
|
%
|
ISO 527
|
|
Tensile Strain, break, 5 mm/min
|
5
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
4790
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
109
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
4440
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, notched, 23°C
|
3
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
3
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C
|
71
|
cm-kgf
|
ASTM D 3763
|
|
Izod Impact, notched 80*10*4 +23°C
|
4
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
3
|
kJ/m2
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
3
|
kJ/m2
|
ISO 179/1eA
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50
|
185
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
185
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
5.95E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
6.49E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, flow
|
5.95E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
6.49E-05
|
1/°C
|
ISO 11359-2
|
|
Vicat Softening Temp, Rate B/50
|
185
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
188
|
°C
|
ISO 306
|
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
184
|
°C
|
ISO 75/Bf
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.24
|
-
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.7 - 0.9
|
%
|
SABIC Method
|
|
Melt Flow Rate, 280°C/5.0 kgf
|
16
|
g/10 min
|
ASTM D 1238
|
|
Density
|
1.24
|
g/cm3
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
3.6
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.7
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 220°C/5.0 kg
|
14
|
cm3/10 min
|
ISO 1133
|
|
Source GMD, last updated:2007/12/21
|
|
? Do NOT mix NORYL GTX* resin with other grades of NORYL* resins.
|
|
Parameter
|
|
Injection Molding
|
Value
|
Unit
|
|
Drying Temperature
|
95 - 105
|
°C
|
|
Drying Time
|
3 - 4
|
hrs
|
|
Drying Time (Cumulative)
|
8
|
hrs
|
|
Maximum Moisture Content
|
0.07
|
%
|
|
Minimum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
275 - 300
|
°C
|
|
Nozzle Temperature
|
275 - 300
|
°C
|
|
Front - Zone 3 Temperature
|
270 - 300
|
°C
|
|
Middle - Zone 2 Temperature
|
265 - 300
|
°C
|
|
Rear - Zone 1 Temperature
|
260 - 300
|
°C
|
|
Mold Temperature
|
65 - 95
|
°C
|
|
Back Pressure
|
0.3 - 1.4
|
MPa
|
|
Screw Speed
|
20 - 100
|
rpm
|
|
Shot to Cylinder Size
|
30 - 50
|
%
|
|
Vent Depth
|
0.013 - 0.038
|
mm
|
|
|
|
|
|
|
    