點(diǎn)擊圖片查看大圖| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 物理性能 | 熔體流動(dòng)速率 | ASTM D-1238 | 10 | g/10min | |
| 吸收率 | 23℃ 60%RH | ASTM D-570 | 0.22 | % | |
| 比重 | ASTM D-792 | 1.41 | |||
| 成型收縮率 | t3mm 直徑100mm | 2.0 | % | ||
| 機(jī)械性能 | 拉伸強(qiáng)度 | 23℃ | ASTM D-638 | 560 | kgf/cm2 |
| 彎曲強(qiáng)度 | 23℃ | ASTM D-790 | 780 | kgf/cm2 | |
| 洛氏硬度 | ASTM D-785 | 80 | M | ||
| 伸長(zhǎng)率 | 23℃ | ASTM D-638 | 85 | % | |
| 拉伸沖擊強(qiáng)度 | t3.2mm Stype | ASTM D-1822 | 105 | kgf.cm/cm2 | |
| 彎曲彈性率 | 23℃ | ASTM D-790 | 2.50×104 | kgf/cm2 | |
| 斷裂強(qiáng)度 | t2mm | ASTM D-732 | 540 | kgf/cm2 | |
| Izod缺口沖擊強(qiáng)度 | Notch t3.2mm | ASTM D-256 | 6.5 | kgf.cm/cm | |
| 電氣性能 | 體積電阻率 | ASTM D-257 | 1×1014 | Ω.cm | |
| 表面電阻率 | ASTM D-257 | 1×1016 | Ω | ||
| 熱性能 | 阻燃性 | t0.8mm | UL-94 | HB | |
| 熱變形溫度 | 18.6kgf/cm2 | ASTM D-648 | 110 | ℃ | |
| 熔點(diǎn) | 10℃/min | DSC Method | 165 | ℃ | |
| 熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 150 | ℃ | |
| 線性膨脹系數(shù) | 20℃ -80℃ | ASTM D-696 | 13×10-5 | ℃ | |
| 如需查詢更多產(chǎn)品信息，請(qǐng)前往公司主營(yíng)網(wǎng)站http://qianqiuguoji.1688.com | |
| 聯(lián)系人: | 李正強(qiáng)經(jīng)理 |
| 聯(lián)系手機(jī): | 15335258581 |
| 公司電話: | 0512-86895007 |
| 客服Q Q: | 2078002886 |
| 郵箱: | 2078002886@qq.com |
| 傳真: | 0512-86895003（請(qǐng)注明李正強(qiáng)經(jīng)理收） |