點(diǎn)擊圖片查看大圖
| 物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
密度 / 比重 | |||
-- |
| ASTM D792 | |
-- | 1.17 | g/cm3 | ISO 1183 |
特定體積 | 23.5 | in3/lb | ASTM D792 |
熔流率（熔體流動(dòng)速率） | |||
250°C/2.16 kg | 3.8 | g/10 min | ASTM D1238 |
250°C/5.0 kg | 11 | g/10 min | ASTM D1238, ISO 1133 |
265°C/2.16 kg | 6.0 | g/10 min | ASTM D1238 |
266°C/5.0 kg | 20 | g/10 min | ASTM D1238 |
250°C/2.16 kg | 3.0 | g/10 min | ISO 1133 |
熔融體積流量（MVR） | ISO 1133 | ||
250°C/2.16 kg | 3.00 | cm3/10min | |
250°C/5.0 kg | 10 | cm3/10min | |
265°C/2.16 kg | 6.00 | cm3/10min | |
265°C/5.0 kg | 18 | cm3/10min | |
收縮率 - 流動(dòng) (0.126 in) | 1.0 到 1.2 | % | 內(nèi)部方法 |
吸水率 | ISO 62 | ||
飽和, 73°F | 0.28 | % | |
平衡, 73°F, 50% RH | 0.080 | % |
| 機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
拉伸模量 | |||
-- 2 | 265000 | psi | ASTM D638 |
-- 3 | 265000 | psi | 內(nèi)部方法 |
-- 4 | 263000 | psi | ASTM D638 |
-- | 260000 | psi | ISO 527-2/1 |
抗張強(qiáng)度 | |||
屈服 5 | 6820 | psi | ASTM D638 |
屈服 6 | 6530 | psi | 內(nèi)部方法 |
屈服 7 | 6380 | psi | ASTM D638 |
屈服 | 6380 | psi | ISO 527-2/5 |
屈服 | 6820 | psi | ISO 527-2/50 |
斷裂 7 | 7250 | psi | ASTM D638 |
斷裂 6 | 6820 | psi | 內(nèi)部方法 |
斷裂 5 | 6960 | psi | ASTM D638 |
斷裂 | 6240 | psi | ISO 527-2/5, ISO 527-2/50 |
伸長(zhǎng)率 | |||
屈服 7 | 4.6 | % | ASTM D638 |
屈服 6 | 4.6 | % | 內(nèi)部方法 |
屈服 5 | 4.0 | % | ASTM D638 |
屈服 | 4.1 | % | ISO 527-2/5 |
屈服 | 4.6 | % | ISO 527-2/50 |
斷裂 7 | 120 | % | ASTM D638 |
斷裂 6 | 110 | % | 內(nèi)部方法 |
斷裂 5 | 120 | % | ASTM D638 |
斷裂 | 110 | % | ISO 527-2/5 |
斷裂 | 120 | % | ISO 527-2/50 |
彎曲模量 | |||
1.97 in 跨距 8 | 241000 | psi | ASTM D790 |
-- 9 | 270000 | psi | ISO 178 |
彎曲應(yīng)力 | |||
-- 9, 10 | 10300 | psi | ISO 178 |
屈服, 1.97 in 跨距 8 | 10200 | psi | ASTM D790 |
斷裂, 1.97 in 跨距 8 | 10000 | psi | ASTM D790 |
| 沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 11 | ISO 179/1eA | ||
-22°F | 22 | ft·lb/in2 | |
73°F | 26 | ft·lb/in2 | |
懸壁梁缺口沖擊強(qiáng)度 | |||
-40°F | 11 | ft·lb/in | ASTM D256 |
-22°F | 12 | ft·lb/in | ASTM D256 |
-4°F | 13 | ft·lb/in | ASTM D256 |
14°F | 12 | ft·lb/in | ASTM D256 |
32°F | 13 | ft·lb/in | ASTM D256 |
73°F | 14 | ft·lb/in | ASTM D256 |
-40°F 12 | 22 | ft·lb/in2 | ISO 180/1A |
-22°F 12 | 23 | ft·lb/in2 | ISO 180/1A |
-4°F 12 | 24 | ft·lb/in2 | ISO 180/1A |
14°F 12 | 25 | ft·lb/in2 | ISO 180/1A |
32°F 12 | 26 | ft·lb/in2 | ISO 180/1A |
73°F 12 | 26 | ft·lb/in2 | ISO 180/1A |
裝有測(cè)量?jī)x表的落鏢沖擊 | ASTM D3763 | ||
-40°F, Energy at Peak | 434 | in·lb | |
-40°F, Total Energy | 522 | in·lb | |
-22°F, Energy at Peak | 434 | in·lb | |
-22°F, Total Energy | 540 | in·lb | |
-4°F, Energy at Peak | 363 | in·lb | |
-4°F, Total Energy | 469 | in·lb | |
73°F, Energy at Peak | 389 | in·lb | |
73°F, Total Energy | 478 | in·lb |
| 熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
載荷下熱變形溫度 | |||
66 psi, 未退火, 0.126 in | 226 | °F | ASTM D648 |
66 psi, 未退火, 0.252 in | 243 | °F | ASTM D648 |
66 psi, 未退火, 0.157 in, 2.52 in 跨距 12 | 228 | °F | ISO 75-2/Bf |
264 psi, 未退火, 0.126 in | 181 | °F | ASTM D648 |
264 psi, 未退火, 0.252 in | 203 | °F | ASTM D648 |
264 psi, 未退火, 0.157 in, 2.52 in 跨距 12 | 189 | °F | ISO 75-2/Af |
維卡軟化溫度 | |||
-- | 246 | °F | ASTM D1525 13, ISO 306/B50 13 |
-- | 252 | °F | ISO 306/B120 |
線形熱膨脹系數(shù) | |||
流動(dòng) : -40 到 203°F | 5.4E-5 | in/in/°F | ASTM E831 |
流動(dòng) : -22 到 176°F | 5.4E-5 | in/in/°F | ISO 11359-2 |
垂直 : -40 到 203°F | 5.6E-5 | in/in/°F | ASTM E831 |
垂直 : -22 到 176°F | 5.6E-5 | in/in/°F | ISO 11359-2 |
| 注射 | 額定值 | 單位制 | |
干燥溫度 | 230 | °F | |
干燥時(shí)間 | 4.0 到 6.0 | hr | |
建議的大水分含量 | 0.020 | % | |
建議注射量 | 50 到 80 | % | |
料筒后部溫度 | 473 到 509 | °F | |
料筒中部溫度 | 482 到 518 | °F | |
料筒前部溫度 | 491 到 527 | °F | |
射嘴溫度 | 491 到 518 | °F | |
加工（熔體）溫度 | 500 到 527 | °F | |
模具溫度 | 149 到 194 | °F | |
背壓 | 43.5 到 102 | psi | |
螺桿轉(zhuǎn)速 | 50 到 80 | rpm | |
排氣孔深度 | 5.1E-4 到 7.9E-4 | in |
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。