點(diǎn)擊圖片查看大圖| Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, break | 1980 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, break | 3 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 175000 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress | 2950 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus | 143400 | kgf/cm2 | ASTM D 790 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 103 | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 13 | cm-kgf/cm | ASTM D 256 | |
| THERMAL | Value | Unit | Standard | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 212 | °C | ASTM D 648 | |
| PHYSICAL | Value | Unit | Standard | |
| Density | 1.3 | g/cm3 | ASTM D 792 | |
| Property |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yield | 1720 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, break | 1610 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yield | 1.8 | % | ASTM D 638 | |
| Tensile Strain, break | 1.9 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 168700 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress | 2460 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus | 133500 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield | 162 | MPa | ISO 527 | |
| Tensile Stress, break | 162 | MPa | ISO 527 | |
| Tensile Strain, yield | 1.6 | % | ISO 527 | |
| Tensile Strain, break | 1.6 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 15750 | MPa | ISO 527 | |
| Flexural Stress | 239 | MPa | ISO 178 | |
| Flexural Modulus | 13000 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 54 | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 5 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Energy @ peak, 23°C | 42 | cm-kgf | ASTM D 3763 | |
| Multiaxial Impact | 20 | cm-kgf | ISO 6603 | |
| Izod Impact, unnotched 80*10*4 +23°C | 32 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 217 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 200 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 5.58E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.98E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, flow | 5.7E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow | 1.9E-05 | 1/°C | ISO 11359-2 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 218 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 198 | °C | ISO 75/Af | |
| PHYSICAL | Value | Unit | Standard | |
| Density | 1.52 | g/cm3 | ASTM D 792 | |
| Moisture Absorption, 50% RH, 24 hrs | 0.1 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 24 hrs (5) | 0.1 | % | ASTM D 955 | |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.8 | % | ASTM D 955 | |
| Mold Shrinkage, flow, 24 hrs (5) | 0.11 | % | ISO 294 | |
| Mold Shrinkage, xflow, 24 hrs (5) | 0.78 | % | ISO 294 | |
| Wear Factor Washer | 444 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified | |
| Dynamic COF | 0.34 | - | ASTM D 3702 Modified | |
| Static COF | 0.28 | - | ASTM D 3702 Modified | |
| Density | 1.52 | g/cm3 | ISO 1183 | |
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。