Physical PropertiesMetricEnglishCommentsMechanical PropertiesMetricEnglishCommentsThermal PropertiesMetricEnglishCommentsProcessing PropertiesMetricEnglishComments
| ? | |||
| Density? | 1.41?g/cc | 0.0509?lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow? | 0.00250?cm/cm | 0.00250?in/in | 60x60x2; 280 °C / MT 80°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse? | 0.00730?cm/cm | 0.00730?in/in | 60x60x2; 280 °C / MT 80°C; 600 bar; ISO 294-4 |
| ? | |||
|
Puncture Resistance? |
1100?N @Temperature -30.0 °C |
247?lb (f) @Temperature -22.0 °F |
ISO 6603-2 |
| ? |
1450?N @Temperature 23.0 °C |
326?lb (f) @Temperature 73.4 °F |
ISO 6603-2 |
| Tensile Strength at Break? | 160?MPa | 23200?psi | 5 mm/min; ISO 527-1,-2 |
| Elongation at Break? | 5.50 % | 5.50 % | 5 mm/min; ISO 527-1,-2 |
| Tensile Modulus? | 11.0?GPa | 1600?ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength? | 225?MPa | 32600?psi | 2 mm/min; ISO 178-A |
| Flexural Yield Strength? |
235?MPa @Strain 3.50 % |
34100?psi @Strain 3.50 % |
2 mm/min; ISO 178-A |
| Flexural Modulus? | 10.1?GPa | 1460?ksi | 2 mm/min; ISO 178-A |
| Flexural Strain at Break? | 5.00 % | 5.00 % | 2 mm/min; ISO 178-A |
|
Izod Impact, Notched (ISO)? |
17.0?kJ/m2 @Temperature -30.0 °C |
8.09?ft-lb/in2 @Temperature -22.0 °F |
ISO 180-1A |
| ? |
28.0?kJ/m2 @Temperature 23.0 °C |
13.3?ft-lb/in2 @Temperature 73.4 °F |
ISO 180-1A |
|
Izod Impact, Unnotched (ISO)? |
95.0?kJ/m2 @Temperature 23.0 °C |
45.2?ft-lb/in2 @Temperature 73.4 °F |
ISO 180-1U |
| ? |
95.0?kJ/m2 @Temperature -30.0 °C |
45.2?ft-lb/in2 @Temperature -22.0 °F |
ISO 180-1U |
|
Charpy Impact Unnotched? |
10.5?J/cm2 @Temperature -30.0 °C |
50.0?ft-lb/in2 @Temperature -22.0 °F |
ISO 179-1eU |
| ? |
11.0?J/cm2 @Temperature 23.0 °C |
52.3?ft-lb/in2 @Temperature 73.4 °F |
ISO 179-1eU |
|
Charpy Impact, Notched? |
1.70?J/cm2 @Temperature -30.0 °C |
8.09?ft-lb/in2 @Temperature -22.0 °F |
ISO 179 1eA |
| ? |
2.80?J/cm2 @Temperature 23.0 °C |
13.3?ft-lb/in2 @Temperature 73.4 °F |
ISO 179 1eA |
|
Puncture Energy? |
4.70?J @Temperature -30.0 °C |
3.47?ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
| ? |
9.10?J @Temperature 23.0 °C |
6.71?ft-lb @Temperature 73.4 °F |
ISO 6603-2 |
| ? | |||
| Melting Point? | 220?°C | 428?°F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi)? | 203?°C | 397?°F | ISO 75-1,-2 |
| Shrinkage, MD? |
0.0300 % @Treatment Temp. 120 °C, Time 14400 sec |
0.0300 % @Treatment Temp. 248 °F, Time 4.00 hour |
Post-Shrinkage Flow Direction; 60x60x2; ISO 294-4 |
| Shrinkage, TD? |
0.130 % @Treatment Temp. 120 °C, Time 14400 sec |
0.130 % @Treatment Temp. 248 °F, Time 4.00 hour |
60x60x2; ISO 294-4 |
| ? | |||
| Melt Temperature? | 290?°C | 554?°F | injection molding |
| ? | 280?-?300?°C | 536?-?572?°F | |
| Mold Temperature? | 80.0?°C | 176?°F | injection molding |
| ? | 80.0?-?100?°C | 176?-?212?°F | |
| Drying Temperature? | 80.0?°C | 176?°F | |
| Dry Time? | 2.00?-?6.00?hour | 2.00?-?6.00?hour | |
| Moisture Content? | 0.0300 - 0.120 % | 0.0300 - 0.120 % | Karl Fischer |