數(shù)據(jù)提供企業(yè)[ 東莞家興尼龍 ] | 數(shù)據(jù)修正企業(yè)[ 暫無(wú)! ] | |||||
性能項(xiàng)目 | 測(cè)試條件 | 測(cè)試方法 | 數(shù)值/描述 | 單位 | |
機(jī)械性能 | 拉伸強(qiáng)度(引張強(qiáng)度) | ASTM D638/ISO 527 | 155 | kg/cm²(MPa)[Lb/in2] | |
拉伸模量 | ASTM D638/ISO 527 | kg/cm²(MPa)[Lb/in2] | |||
拉伸屈服伸長(zhǎng)率(延伸率) | ASTM D638/ISO 527 | % | |||
拉伸斷裂伸長(zhǎng)率(延伸率) | ASTM D638/ISO 527 | % | |||
彎曲模量(彎曲彈性率) | ASTM D790/ISO 178 | 16000 | kg/cm²(MPa)[Lb/in2] | ||
彎曲強(qiáng)度 | ASTM D790/ISO 178 | 220 | kg/cm²(MPa)[Lb/in2] | ||
IZOD 缺口沖擊強(qiáng)度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
Charpy沖擊強(qiáng)度 | 23℃ (缺口) | ASTM D256/ISO 179 | 12 | kg·cm/cm(J/M)ft·lb/in | |
-30℃(缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
23℃(無(wú)缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
-30℃(無(wú)缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
物性性能 | 比重(密度) | ASTM D792/ISO 1183 | 1.66 | ||
吸水率 23℃/24H | ASTM D570/ISO 62 | % | |||
熱性能 | 熱變形溫度 | 退火 | ASTM D648/ISO 75 | 340 | ℃(℉) |
未退火 | ASTM D648/ISO 75 | ℃(℉) | |||
熔點(diǎn) | - | ℃(℉) | |||
燃燒性(率) | UL94 | ||||
線性膨脹系數(shù) | ASTM D696/ISO 11359 | mm/mm.℃ | |||
電氣性能 | 介電常數(shù) | 100HZ | ASTM D150/IEC 60250 | ||
1MHZ | ASTM D150/IEC 60250 | ||||
介電損耗 | 100HZ | ASTM D150/IEC 60250 | |||
1MHZ | ASTM D150/IEC 60250 | ||||
體積電阻率 | ASTM D257/IEC 60093 | Ω.cm | |||
表面電阻率 | ASTM D257/IEC 60093 | Ω | |||
耐電弧性 | ASTM D495/IEC 60112 | 138 | |||
加工條件 | 干燥條件 | ||||
加工溫度 | 射嘴 | ℃ | |||
料筒前段 | ℃ | ||||
料筒中段 | ℃ | ||||
料筒后段 | ℃ | ||||
熔體溫度 | ℃ | ||||
模具溫度 | ℃ | ||||
壓力 | 注塑壓力 | Mpa | |||
保壓壓力 | Mpa | ||||
背壓 | Mpa | ||||
螺桿轉(zhuǎn)速 | rpm | ||||
其他 | 備注 | ||||
顏色 | VF2001/BK010P | ||||
特性 | 超高耐熱,高溫剛性,玻璃纖維,標(biāo)準(zhǔn) | ||||
用途 |
LCP 日本寶理 S135