Teijin Panlite? L-1225L（塑膠原料-聚碳酸酯-PC塑料）

Physical Properties物理性質(zhì)

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Density 比重

1.20 g/cc

0.0434 lb/in3

ISO 1183

Water Absorption 吸水率

0.20 %

0.20 %

in water, 23°C, 24h; ISO 62

Linear Mold Shrinkage 線性收縮率

0.0050 - 0.0070 cm/cm
@Thickness 4.00 mm

0.0050 - 0.0070 in/in
@Thickness 0.157 in

Linear Mold Shrinkage, Transverse 線性收縮率/橫向斷裂拉伸強(qiáng)度

0.0050 - 0.0070 cm/cm
@Thickness 4.00 mm

0.0050 - 0.0070 in/in
@Thickness 0.157 in

Melt Flow 熔體流動(dòng)速率

21.6 g/10 min
@Load 1.20 kg,
Temperature 300 °C

21.6 g/10 min
@Load 2.65 lb,
Temperature 572 °F

ISO 1133

Mechanical Properties力學(xué)性能

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Tensile Strength, Yield 屈服拉伸強(qiáng)度

61.0 MPa

8850 psi

50mm/min; ISO 527

Elongation at Break 斷裂伸長(zhǎng)率

>= 50 %

>= 50 %

50mm/min; ISO 527

Elongation at Yield 屈服伸長(zhǎng)率

6.0 %

6.0 %

50mm/min; ISO 527

Tensile Modulus 拉伸模量

2.40 GPa

348 ksi

1mm/min; ISO 527

Flexural Strength 彎曲強(qiáng)度

93.0 MPa

13500 psi

2mm/min; ISO 178

Flexural Modulus 彎曲彈性模量

2.35 GPa

341 ksi

2mm/min; ISO 178

Charpy Impact Unnotched 夏比缺口試樣沖擊

NB

NB

ISO 179

Charpy Impact, Notched 夏比缺口沖擊

6.70 J/cm2

31.9 ft-lb/in2

ISO 179

Electrical Properties電性能

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Volume Resistivity 體積電阻率

>= 1.00e+13 ohm-cm

>= 1.00e+13 ohm-cm

IEC 60093

Surface Resistance 表面電阻

>= 1.00e+15 ohm

>= 1.00e+15 ohm

IEC 60093

Dielectric Constant 介電常數(shù)

3.0
@Frequency 1e+6 Hz

3.0
@Frequency 1e+6 Hz

IEC 60250

3.1
@Frequency 100 Hz

3.1
@Frequency 100 Hz

IEC 60250

Dielectric Strength 介電強(qiáng)度

30.0 kV/mm

762 kV/in

IEC 60243

Dissipation Factor 耗散因數(shù)

0.0010
@Frequency 100 Hz

0.0010
@Frequency 100 Hz

IEC 60250

0.0090
@Frequency 1e+6 Hz

0.0090
@Frequency 1e+6 Hz

IEC 60250

Comparative Tracking Index 跟蹤指數(shù)

250 V

250 V

IEC 60112

Thermal Properties熱性能

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

CTE, linear 線性熱膨脹系數(shù)

70.0 μm/m-°C
@Temperature 20.0 °C

38.9 μin/in-°F
@Temperature 68.0 °F

ISO 11359

CTE, linear, Transverse to Flow 線性熱膨脹系數(shù)/橫向

70.0 μm/m-°C
@Temperature 20.0 °C

38.9 μin/in-°F
@Temperature 68.0 °F

ISO 11359

Deflection Temperature at熱變形溫度 0.46 MPa (66 psi) 

139 °C

282 °F

ISO 75

Deflection Temperature at熱變形溫度 1.8 MPa (264 psi) 

126 °C

259 °F

ISO 75

Vicat Softening Point 維卡軟化點(diǎn)

146 °C

295 °F

50°C/hr, 50N; ISO 306

UL RTI, Electrical 相對(duì)溫度指數(shù)

125 °C
@Thickness 1.47 mm

257 °F
@Thickness 0.0579 in

UL 746B

UL RTI, Mechanical with Impact 機(jī)械沖擊熱指數(shù)

115 °C
@Thickness 1.47 mm

239 °F
@Thickness 0.0579 in

UL 746B

UL RTI, Mechanical without Impact無(wú)機(jī)械沖擊熱指數(shù) 

125 °C
@Thickness 1.47 mm

257 °F
@Thickness 0.0579 in

UL 746B

Flammability, UL94 阻燃等級(jí)

HB
@Thickness 1.90 mm

HB
@Thickness 0.0748 in

V-2
@Thickness 0.400 mm

V-2
@Thickness 0.0157 in

Optical Properties光學(xué)性質(zhì)

Metric公制數(shù)據(jù)

English英制數(shù)據(jù)

Comments測(cè)試方法

Refractive Index 折射率

1.585

1.585

ASTM D542

Transmission, Visible 透光率

88 %
@Thickness 3.00 mm

88 %
@Thickness 0.118 in

ASTM D1003